Stainless Steel Welding wire 316L Flux Core
Introduction & Characteristics:
FRW-316L is a rutile type flux cored wire for low carbon 18%Cr-12%Ni-2%Mo stainelss steel. It is used for all position welding to be used with CO2 or Argon + CO2 mixed shielding gases.This wire recommended for high deposition rates in the flat and horizbontal position.
Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2. Designed for welding with CO2 or Argon + CO2 mixed shielding gases
3. When welding, the gas flow rate is generally 20~25L/min.
Chemical compostiton of deposited metal (shield gas:CO2)
Introduction & Characteristics:
FRW-316L is a rutile type flux cored wire for low carbon 18%Cr-12%Ni-2%Mo stainelss steel. It is used for all position welding to be used with CO2 or Argon + CO2 mixed shielding gases.This wire recommended for high deposition rates in the flat and horizbontal position.
Instructions:
1.The oil stains and rust on the weldments should be cleared away.
2. Designed for welding with CO2 or Argon + CO2 mixed shielding gases
3. When welding, the gas flow rate is generally 20~25L/min.
Chemical compostiton of deposited metal (shield gas:CO2)
| C | Mn | Si | P | S | Ni | Cr | Mo |
| 0.027 | 1.51 | 0.4 | 0.026 | 0.003 | 12.75 | 19.61 | 2.28 |
Mechanical properties of deposited metal (shield gas:CO2
| Yield Strength | Elongation | Impact Value |
| Mpa(σb) | %(δ5) | 0ºC(J) |
| 580 | 45 | 32 |
Sizes available and recommended currents(DC-EP)
| Diameter(mm) | 0.9 | 1.2 | 1.6 | |
| Current(A) | F,HF | 130-180 | 180-220 | 250-290 |
| V-up OH | 100-140 | 120-160 | 220-270 | |