Basic Info.
Model NO.
H08MnMoA(EA2)
Net Weight (Kg)
1kg\5kg\15kg\17kg\18kg\20kg
C Composition(%)
0.06~0.15
Mn Composition(%)
1.40~1.85
Si Composition(%)
0.80~1.15
P Composition(%)
≤0.025
S Composition(%)
≤0.035
Cu Composition(%)
≤0.50
Yield Strength (MPa)
≥420
Tensile Strength (MPa)
≥500
Transport Package
72spool /Pallet, 22pallets/20FT Container
Specification
CE, ISO9001, ABS, LR, CCS, DB, TUV.
Trademark
Marink Or OEM
Origin
Qingdao, China
HS Code
7229200000
Production Capacity
4000 Metric Tons Per Month
Product Description
Application: Conform with: |
| Wire Type | Size | inner diameter | outer diameter | Net Weight |
| Coil Packaging | φ1.6~5.0(mm) | 300mm 620mm | 400mm 820mm | 25kg 250kg |
| TIG Wire | 1 meter | 5kg | ||
| chemical composition of welding wire(%) | C | Mn | Si | P | S | Cr | Ni | Mo | Ti | Cu |
| ≤0.10 | 1.20~1.60 | ≤0.25 | ≤0.030 | ≤0.030 | ≤0.20 | ≤0.30 | 0.30~0.50 | 0.15 | ≤0.20 |
| Mechanical Properties or Deposited Metal | Yield strengthσ0.2(Mpa) | Tensile strengthσb(Mpa) | Elongationδ5(%) | AKV impact(J) |
| ≥440 | ≥540 | ≥17 | ≥27(-20) |
| Paul welding gas | SAW | |||||||
| Wire Size | φ0.8 | φ1.0 | φ1.2 | φ1.6 | φ2.0 | φ3.0 | φ4.0 | φ5.0 |
| Please be noted | Welding position | |||||||
| Wire shall be stocked in dry.open the packs just when welding to avoid the wire rust. Before welding please clean out the oil,rust,water etc from the work parts | ||||||||